تحضير وخصائص أغشية كبريتيد الزنك ZnSالمرسبة بالحمام الكيميائي C

Abstract

In this thesis, Zinc sulphide (ZnS) thin films were prepared by chemical bath deposition process. The deposition was carried out at a temperature of 80°C with different deposition times )2h, 3h and 4h(. The effect of the deposition times on the structural and optical properties of these films was investigated. The X-ray diffraction spectra of chemically deposited ZnS thin films showed the amorphous structure of the films deposited with 2h and 3h while, that deposited with 4 h showed crystallize structure. The optical properties, including the transmission spectra, absorption coefficient and band gap energy of these films were studied. It is observed that the band gap values decreases with increasing time deposition. In the case of CBD films, band gap values varied from 3.6 to 3.9 eV. It’s noticed that the optical properties were influenced by the duration of depositionحضًٍ انبحث دساست حأثيش يذة انخشسيب عهي انخواص انبُيويت وانبصشيت نغشاء كبشيخيذ انضَك ( ،)ZnSانًحضش بإسخخذاو حقُيت انخشسيب بانحًاو انكيًيائي ( )CBDفي أصيُت يخخهفت (،)4h،3h،2h وقذ حى ححضيش هزِ الاغشيت في دسجت حشاسة (° ،)80 Cحيث بيُج َخائج فحوصاث الاشعت انسيُيت ( )DRXاٌ انغشاء رو حشكيب عشوائي ( )Amorphusبانُسبت نهششائح انًشسبت في ()3h،2h ويخبهوسة بانُسبت نهششيحت انًشسبت في (. )4hوحضًُج دساست انخواص انبصشيت يٍ خلال اطياف: انُفاريت، يعايم الايخصاص، انفاصم انطاقي...،.وقذ نوحظ أٌ صيادة يذة انخشسيب أدى اني َقصاٌ قيى انفاصم انطاقي حيث حخشاوح حوني[ 3,6ـ ،]3,9 eVوكاٌ نضيادة يذة انخشسيب حأثيش عهي يخخهف انثوابج انبصشيت